Mix By Volume: 3oz to 1ozMix by Weight: 100 to 33 (example) by weight provides best results
Tensile Strength: 10,800Tensile Modulus: 420,000Flexural Strength: 14,000Flexural Modulus: 510,000Barcol Hardness: 84HDT: 125FCompression Yield: 15,900Elongation%: 3.3
Pot Life: 45min at 77F (room temp) - Set time approx 5 hoursViscosity: 1000 (medium)
WINTER WARNING:Cold temperatures and increased moisture can play havoc with your project. When mixing in the cold months please let the mixed epoxy stand in the mixing cup for a minute or two to allow the exothermic reaction to really kick in. Quickly mixing and pouring out your epoxy can kill this process and impede the quality of your cure.THIS IS A 3:1 EPOXY SYSTEM......NOT THE LESS EXPENSIVE LOWER PERFORMING 2:1 MIX
This epoxy is designed for use with high performance fabrics such as Carbon Fiber, Kevlar/Aramids, Basalt, fiberglass. It has a non-blushing characteristic, low vapor, excellent color, high gloss, excellent resistance to water vapor pressure, excellent U.V. stability and high strength. Also contains an opticalbrighter.
Contains opticalenhancers giving it an interesting blue color prior to mix/cure.
All purpose vacuum bagging, marine, transportation, architectural, and general composites, surf and sailboards, hand lay up applications, gloss coatings and just about anything else that needs to be tough.
Whats Delivered: 18 ounces ofepoxy resin and 6 ounces of hardener = 24 ounces.(mix 3 parts epoxy resin to 1 part hardener best results when weighed out)
Instructions Included