20% Carbon Fiber Reinforced PA6 - Exceptional Performance for Your Projects

Experience the unparalleled strength and durability of Fiberon PA6-CF20, a cutting-edge material designed for high-performance applications. This innovative filament combines Nylon 6 with 20% carbon fiber, making it ideal for a variety of demanding uses.

Key Features:

• High Stiffness & Strength: Achieve superior dimensional stability and strong layer adhesion, perfect for rigid functional parts, tooling, fixtures, and prototypes.
• Engineering Performance After Annealing: Enjoy impressive TDS values with a dry X-Y tensile strength of 109.3 MPa and a Young’s modulus of 8.64 GPa. Heat deflection temperature reaches 215°C at 0.45 MPa after proper annealing.
• Moisture Sensitivity Management: Ensure optimal printing results by drying the filament at 100°C for 10 hours before use. Store and print in conditions below 20% relative humidity to minimize issues like stringing and bubbles.
• Advanced Printer Setup Required: Utilize a nozzle temperature of 280–300°C and a build plate temperature of 40–50°C. An all-metal hotend is recommended with the cooling fan turned off for best results.
• Wear-Resistant Nozzle Needed: Due to the abrasive nature of carbon fiber, use a hardened steel or ruby nozzle instead of standard brass. For enhanced heat resistance and stability, anneal printed parts at 100°C for 16 hours.

Printing Tips:

• Confirm smooth filament routing and unrestricted spool rotation before starting long prints.
• Achieve printing speeds up to 300 mm/s with a properly tuned profile.

This advanced filament is your go-to solution for creating robust prototypes and functional parts that demand high performance. Elevate your projects with Fiberon PA6-CF20 today!