Polymaker Fiberon PPS-CF10 1.75mm 3KG Black Carbon Fiber Filament High Temp

by Polymaker

Key features

• Carbon Fiber Reinforced PPS: Fiberon PPS-CF10 is a 1.75 mm carbon fiber reinforced PPS filament engineered for high heat resistance, chemical resistance, rigidity, and dimensional stability. Suitable for high-temperature prototypes, tooling, fixtures, electronics components, and industrial functional parts.
• High Heat Resistance: After annealing at 125°C for 16 hours, PPS-CF10 has a typical heat deflection temperature of 252.5°C at 0.45 MPa under the test conditions specified in the product TDS. Actual part performance may vary with part design, printing parameters, annealing conditions, and operating environment.
• Low Moisture Absorption: PPS-CF10 has an equilibrium moisture absorption of approximately 0.225% at 23°C and 70% relative humidity. For consistent extrusion and surface quality, dry at 100°C for 10 hours before printing and keep the filament below 20% relative humidity during storage and use.
• Direct Filament Path Recommended: As a short-carbon-fiber reinforced engineering filament, PPS-CF10 is stiff before printing. Sharp bends, tightly curved PTFE tubes, or multiple feeder turns can place excessive stress on the filament. Use a smooth, low-resistance, and direct path from the dry box to the extruder. Proper printing conditions produce rigid, dimensionally stable functional parts.
•